Did not do much today but did inspect the painting that was done two years ago. This area knocked down to bare metal well and had naval jelly applied before painting. It has held up well and only need minor touch up.
I thought this went as well as above when prep and painting was done, dont remember if any treatment was applied here. Im getting rust creap here and though the rust got knocked off well, so not sure what is up with this area.
This area has a bunch of issues and know there cause. The steering box and shock tower came loose at one point, so there is some chipping from that. By the body mount, I tied to rush it with a heat gun and the rippled paint is chipping. Too the right of shock tower, that was deep embedded rust and the treatment did not hold up. I think the spray on can was used here, rust on the inside of the frame was just as bad in that area.
I did not want to contort myself any more after dealing with the under side of the crossmember. So dont think I sanded the spray can treatment well and is showing such.
Yes I could had cleaned this area for show and tell. This area was a rust nightmare and see I gave up too soon messing with the naval jelly.
The naval jelly dose something but is weak at 12% phosphoric acid. So went looking for something stronger and found this that I would estimate at 30%, its listed at 15% when mixed with water. I would rather not deal with muriatic acid, so will see if can get this to work better.
It just gose in a squirt bottle...
Then can spray it on areas I want experiamet on. Some saran wrap would keep it active for longer and not sure if is needed right now, so will see where this gose.
You must be registered for see images
I thought this went as well as above when prep and painting was done, dont remember if any treatment was applied here. Im getting rust creap here and though the rust got knocked off well, so not sure what is up with this area.
You must be registered for see images
This area has a bunch of issues and know there cause. The steering box and shock tower came loose at one point, so there is some chipping from that. By the body mount, I tied to rush it with a heat gun and the rippled paint is chipping. Too the right of shock tower, that was deep embedded rust and the treatment did not hold up. I think the spray on can was used here, rust on the inside of the frame was just as bad in that area.
You must be registered for see images
I did not want to contort myself any more after dealing with the under side of the crossmember. So dont think I sanded the spray can treatment well and is showing such.
You must be registered for see images
Yes I could had cleaned this area for show and tell. This area was a rust nightmare and see I gave up too soon messing with the naval jelly.
You must be registered for see images
The naval jelly dose something but is weak at 12% phosphoric acid. So went looking for something stronger and found this that I would estimate at 30%, its listed at 15% when mixed with water. I would rather not deal with muriatic acid, so will see if can get this to work better.
You must be registered for see images
It just gose in a squirt bottle...
You must be registered for see images
Then can spray it on areas I want experiamet on. Some saran wrap would keep it active for longer and not sure if is needed right now, so will see where this gose.